北欧化工Borealis 耐化学性PP BB125MO
发布时间:2024-11-23
Borealis PP BB125MO
Polypropylene Copolymer
Borealis AG
产品说明:
BB125MO is a heterophasic copolymer. This grade is a low melt flow rate grade intended for blow moulding and sheet extrusion, and features extremely good processability with improved melt strength and melt stability. As all polypropylenes, this grade shows excellent stress-cracking and chemical resistances.
This polymer is one of the IMP (improved mechanical stability) grades, and is characterized by very high stiffness without any loss of impact strength even at low temperatures.
物性信息:
特性 | 刚性,高 高 ESCR(抗应力开裂) 共聚物 较高的熔体稳定性 抗撞击性,良好 可加工性,良好 良好的熔体强度 流动性低 耐低温冲击 耐化学性良好 |
用途 | 波形板 工业容器 工业应用 |
形式 | 粒子 |
加工方法 | 吹塑成型 片材挤出成型 |
密度 | 0.905 | g/cm³ | ISO 1183 |
熔流率(熔体流动速率) | ISO 1133 | ||
190°C/5.0 kg | 2.3 | g/10 min | ISO 1133 |
230°C/2.16 kg | 1.3 | g/10 min | ISO 1133 |
230°C/5.0 kg | 6.0 | g/10 min | ISO 1133 |
拉伸模量 | 1300 | MPa | ISO 527-2/50 |
拉伸应力 (屈服) | 25.0 | MPa | ISO 527-2/50 |
拉伸应变 (屈服) | 5.0 | % | ISO 527-2/50 |
弯曲模量 | 1200 | MPa | ISO 178 |
简支梁缺口冲击强度 | ISO 179/1eA | ||
-20°C | 7.0 | kJ/m² | ISO 179/1eA |
23°C | 50 | kJ/m² | ISO 179/1eA |
热变形温度 (0.45 MPa, 未退火) | 85.0 | °C | ISO 75-2/B |
料筒1区温度 | 190 到 220 | °C | |
料筒2区温度 | 190 到 220 | °C | |
料筒3区温度 | 190 到 220 | °C | |
料筒4区温度 | 190 到 220 | °C | |
料筒5区温度 | 190 到 220 | °C | |
熔体温度 | 180 到 220 | °C | |
口模温度 | 180 到 220 | °C |
展开全文
其他新闻
- 北欧化工批发 Borealis 低流量PP BB108E 2024-11-23
- 北欧化工供应 HG385MO 快速成型周期PP 2024-11-23
- 北欧化工供应 HG313MO PP 2024-11-23
- 北欧化工供应PP HG246FB 2024-11-23
- 北欧化工供应PP HG245FB 2024-11-23
- 北欧化工供应PP HF420FB 2024-11-23
- 北欧化工 PP 2024-11-23